Barium hexaferrite ceramic permanent magnets

P. W. Richter, S. Hart
Suid-Afrikaanse Tydskrif vir Natuurwetenskap en Tegnologie | Vol 2, No 1 | a1095 | DOI: https://doi.org/10.4102/satnt.v2i1.1095 | © 1983 P. W. Richter, S. Hart | This work is licensed under CC Attribution 4.0
Submitted: 20 March 1983 | Published: 20 March 1983

About the author(s)

P. W. Richter,, South Africa
S. Hart,, South Africa

Full Text:

PDF (135KB)

Share this article

Bookmark and Share

Abstract

Barium hexaferrite ceramic permanent magnets were manufactured using a locally produced iron oxide. The effect of sintering temperature on the coercivity, remanence, shape of the hysteresis loops, density and shrinkage was studied. The results indicated that grain growth during the sintering process limited the sintering temperature to 1 200 °C for this material in order to obtain satisfactory values for the coercivity, while remanence and density were optimum at a higher sintering temperature of about 1 230 °C.

Keywords

No related keywords in the metadata.

Metrics

Total abstract views: 1320
Total article views: 1712

Reader Comments

Before posting a comment, read our privacy policy.

Post a comment (login required)

Crossref Citations

No related citations found.